| Properties | Method | Units | Aglas SS | Aglas SS PA6 |
|---|
| General |
|---|
| Density | ISO 1183 | g/cm3 | 1,19 | 1,19 |
| Forming temperature | | °C | 150 | 150 |
| Mechanical |
|---|
| Tensile strength | ISO 527 | MPa | 75 | 75 |
| Elongation at break | ISO 527 | % | 4,3 | 4,3 |
| Elastic modulus | ISO 527 | MPa | 3110 | 3110 |
| Flexural strength | ISO 178 | MPa | 118 | 118 |
| Charpy impact | ISO 179 | kJ/m2 | 18 | 19 |
| Thermal |
|---|
| Vicat softening temperature | ISO 306 | °C | 105 | 105 |
| Coeff. of thermal expansion | literature | 1/K | 6,1x10-5 | 6,1x10-5 |
| Max. temperature of use | | °C | 80 | 80 |
| Optical |
|---|
| Light transmission (clear sheet) | ISO 13468 | % | > 91 | > 91 |
| Yellowness index (864 hours) | internal | | 0,1 | 0,1 |
| Acoustic |
|---|
| Weighted sound reduction index DLR | ISO 1793-2 | dB | | |
| 12 mm | | | 28 | 30 |
| 15 mm | | | 29 | 31 |
| 20 mm | | | 31 | 33 |
| Weighted sound reduction category | ISO 1793-2 | dB | | |
| 12 mm | | | B3 | B3 |
| 15 mm | | | B3 | B3 |
| 20 mm | | | B3 | B3 |